Customized Glass Fiber Reinforced PA66 Granules Modified High Tensile Strength Engineering For Thermal Break Profile
Product Introduction:
Nylon/PA66 granules reinforced by fiberglass, with special additives,is blended and extruded by twin screw extruder. It is more suitable for extrusion of thermal break profile.Compared with ordinary granules, it is more conducive to forming.It has certain advantages in speed,surface finish and yield.The performances of nylon thermal break profiles which are made from this material can meet the national standard of China. It can not only be customized according to customer requirements,far exceeding the national standard,but also can add high-efficiency flame retardant to achieve the purpose of flame retardant.
Advantage:
1. Competitive price, free samples, short delivery period.
2. Low smoke and other characteristics.
3. Good wear resistance,self-lubrication,long-term work at high temperature.
4. High CTI value,excellent electrical insulation.
5. Fast crystallization,fast forming,high temperature resistance.
6. Anti-ultraviolet radiation,anti-chemical agent corrosion.
7. High yield,easy start-up,and get less scrap in the early start-up stage.
8. No lack or incomplete of profiles in the production process.
9. There are different formulations for different shapes.
Details of related standard:
- GB/T 23615.1-2009 Accessorial material for architectural aluminum alloy profiles -- Part 1: Thermal barrier strip of polyamide
- EN 14024-2004 Metal profiles with thermal barrier -- Mechanical performance Requirement, proof and tests for assessment
- YS/T 437-2008 Aluminium profiles moment of inertia calculation methods and computing software requirements
- JG/T 174-2005 Thermal barrier strips for construction industry
- GB 5237.6 -2012 Wrought aluminium alloy extruded profiles for architecture -- Part 6: Thermal barrier profiles
- GB/T 8478-2008 Aluminium windows and doors
- GB/T 8484-2008 Graduation and test for thermal insulating properties of doors and windows
- JG 175-2011 Insulating aluminum alloy profiles with thermal barrier for buildings
Polywell PA66 Granules Performance Table
| NO. | Item | Unit | GB/T 23615.1-2009 | PW-Technical specification |
| | Material Properties |
| 1 | Density | g/cm3 | 1.3±0.05 | 1.28-1.35 |
| 2 | Linear expansion coefficient | K-1 | (2.3-3.5)*10-5 | (2.3-3.5)*10-5 |
| 3 | Vicat softening temperature | ºC | ≥230ºC | ≥233ºC |
| 4 | Melting point | ºC | ≥240 | ≥240 |
| 5 | Testing for tensile cracks | - | No cracks | No cracks |
| 6 | Shore hardness | - | 80±5 | 80-85 |
| 7 | Impact strength(Unnotched) | KJ/m2 | ≥35 | ≥38 |
| 8 | Tensile strength(longitudinal) | MPa | ≥80a | ≥82a |
| 9 | Elasticity modulus | MPa | ≥4500 | ≥4550 |
| 10 | Elongation at break | % | ≥2.5 | ≥2.6 |
| 11 | Tensile strength(transverse) | MPa | ≥70a | ≥70a |
| 12 | High temperature tensile strength(transverse) | MPa | ≥45a | ≥47a |
| 13 | Low temperature tensile strength(transverse) | MPa | ≥80a | ≥81a |
| 14 | Water resistance tensile strength(transverse) | MPa | ≥35a | ≥35a |
| 15 | Aging resistance tensile strength(transverse) | MPa | ≥50a | ≥50a |
1. Sample water content less than 0.2% by weight.
2. Norm laboratory condition:(23±2)ºC and (50±10)% relative humidity.
3. The specifications marked with "a" only applies to I-shape strip otherwise, the specifications concluded between supplier and buyer through consultation, shall be written in contract or purchase order.
Application:
It is mainly used for nylon extruding profiles and nylon thermal break extruding strips. The granules produced by our company are special materials for nylon extruding profiles.There are different formulations for different shapes and complexities to ensure the smooth production of nylon profiles.
Packaging & Delivery:
Packaging details:25kg/bag
Delivery details: shipped in 5-10 working days after receiving the payment
Our Company
Zhangjiagang Polywell Engineering Plastics Company is located in the city of Zhangjiagang, Jiangsu Province, China. Our company has devoted more than ten years to the research and development and production of nylon extruding profiles. According to customer reaction, using our PA66 granules for production can get high yiedl, easy start-up, and get less scrap in the early start-up stage. There will be no lack or incomplete of profiles in the production process, thus avoiding material waste.
Contact us:
Pleass feel free to contact us if you have any questions.